Nano Metallic type
RoHS, ISO9001, SGS, En71, FDA, Reach
Steel
Film Forming Matter
Conversion Type
Epoxy Polyester Ral Grey Color Powder Coating for
High/Semi/Matte
60-80um
0 Grade
2h
12 Months
180 Degree/15mins, 200 Degree/10mins
High Voltage Electrostatic Spraying 40-80kv
at About 25 Degree and at Ventilated Indoors
Lined in with Double PE Bags. Packed in Carton Box
Wonder
25kg/CTN
carton size: 39.5cm*30cm*35cm.
China
3907999990
Color | Chrome Color |
Type | Epoxy Polyester Outdoor |
Gloss | 100-130% |
Thickness | 60-80μm |
Hardness | 2H |
Adhesion | 0 Grade |
Curing | 200ºC*10mins / 180ºC*15mins |
Shelf Life | 12 months |
Product Test
Test Item | Test Standard | Testing Results |
Specific Gravity | ≤1.7 | <1 |
Gloss | 100 - 130% | 130% |
Thickness | 60~80цm | 77цm |
Adhesive force | GB/T9286-1998 | 0 grade |
Impact Resistance | GB/T1732-1993 | 50kg.cm no cracks nor stripping |
Salt spray test | GB/T1771-1991 | 500H,no pulverization,gloss protection 80% |
Winding Resistance | GB/T6742-1986 | 3mm no cracks nor stripping |
Pencil Hardness | GB/T6739-1996 | 2H |
UV Resistance | GB/T14522-1993 | 240h △E<1,gloss protection 80% |
Flexibility | GB/T 6742-1986 | 2mm |
Heat & Humidity Resistance | GB/T 1740-1979 | >500 Hours,film gloss slightly lose |
Color | Chrome Color |
Type | Epoxy Polyester Outdoor |
Gloss | 100-130% |
Thickness | 60-80μm |
Hardness | 2H |
Adhesion | 0 Grade |
Curing | 200ºC*10mins / 180ºC*15mins |
Shelf Life | 12 months |
Product Test
Test Item | Test Standard | Testing Results |
Specific Gravity | ≤1.7 | <1 |
Gloss | 100 - 130% | 130% |
Thickness | 60~80цm | 77цm |
Adhesive force | GB/T9286-1998 | 0 grade |
Impact Resistance | GB/T1732-1993 | 50kg.cm no cracks nor stripping |
Salt spray test | GB/T1771-1991 | 500H,no pulverization,gloss protection 80% |
Winding Resistance | GB/T6742-1986 | 3mm no cracks nor stripping |
Pencil Hardness | GB/T6739-1996 | 2H |
UV Resistance | GB/T14522-1993 | 240h △E<1,gloss protection 80% |
Flexibility | GB/T 6742-1986 | 2mm |
Heat & Humidity Resistance | GB/T 1740-1979 | >500 Hours,film gloss slightly lose |